型號
Grade
|
K值
K value
|
相對聚合度
Degree of
polymerizatio
|
特性和應用
Features and Applications
|
|
E68CT/CF
|
68
|
1120
|
漿料粘度低、優良發泡性能、泡孔平均、顏色白。用於高發泡、深壓紋牆紙。
Plastisol exhibits good shelf-life, outstanding foaming characteristics, easy to detach from mould, suitable for compact coating, foaming layer and top layer of artificial leather.
|
|
E68CF
|
68
|
1120
|
漿料穩定、容易脫模、優良發泡性能。應用於人造革發泡、面層和搪膠。
Plastisol exhibits good shelf-life, outstanding foaming characteristics, easy to detach from mould, suitable for compact coating, foaming layer and top layer of artificial leather.
|
|
E70CQ
|
70
|
1230
|
高假塑性、增加漿料粘度。用於汽車底塗、刮塗和人造革發泡層。
Plastisol exhibits psuedoplastic behaviour and viscosity is increased. It is used for auto-underbody coating, knife coating, and foaming layer of artificial leather.
|
|
P70/HT
|
70
|
1230
|
高透明、高亮度、優良抗水/耐候性，漿料容易脫泡、良好黏附力和成品低吸水性能。
Vinnolit® P 70 HT can be easily converted into a plastisol with excellent low water absorption characteristics and has outstanding weathering properties combined with very high thermal stability. Plastisols formed has good gloss and transparency.
|
|
P74CC
|
74
|
1570
|
極低霧化、優良發泡性能、優良壓紋效果。用於車革面層（真空成型）、發泡層
Low atomization, good foamability, suitable for automotive applications such as foam and top coats in vacuum-thermoformed artificial leather with good emboss retention.
|
|
E80/TT
|
80
|
>2000
|
高聚合型號、漿料粘度低、透明、低吸水性、半啞光效果。用於人造革或地板面層。
High molecular weight, plastisol made has low viscosity, good transparency even at thick film applications, and excellent low water absorption. It is perfectly useful for textile coatings, artificial leather and flooring top coats.
|
|
C65V&EXT
|
65
|
975
|
通用型摻混樹脂、降低漿料粘度、控制流變性、增強製品機械性能。用於所有漿料。
Vinnolit® C 65 V & EXT is a suspension homopolymer whose small particle size and narrow particle size distribution are most suited as a blend component in all paste making. Due to its extremely low plasticizer absorption at room temperature, it lowers viscosity of plastisols and reduces dilatancy if present.
|
|
C100V
|
-
|
-
|
極高聚合度摻混樹脂、表面啞光效果或紋理效果。用於特殊塗料、薄膜。
Its a highly polymerised blending resin. Plastisols made exhibit matt finishes which is used in special coatings and films.
|
|
PA5470/5
|
69
|
1175
|
氯醋樹脂、高假塑性、低溫固化、增加黏合強度。用於人造革黏合層和汽車底漆。
The vinyl acetate content in the copolymer gives medium-viscosity plastisols with slightly pseudo-plastic flow properties and can be processed at lower gelling temperatures. It is used in adhering layer of artificial leather and auto-underbody coating.
|
|
C12/62V
|
62
|
840
|
氯醋摻混樹脂、適合低溫應用。用於汽車底漆、油墨、皮革表面處理劑。
Vinnolit® C 12/62 V is a vinyl chloride/ vinyl acetate copolymer extender resin suitable for low temperature use. It is used in auto-underbody coating, inks, and leather surface treatment coating.
|
|
SA1062/7
|
62
|
840
|
氯醋摻混樹脂、低溫固化、增加黏合強度。用於特殊油墨和汽車底塗。
Vinnolit® SA 1062/7 is a white colored vinyl chloride/ vinyl acetate copolymer extender resin. It exhibits improved adhesion to various substrates, such as metal and synthetic fibers. Suited for automotive underbody coating, carpet backing and laminating pastes.
|
|
VK-710
|
-
|
-
|
氯乙烯-丙烯酸酯接枝共聚物、抗衝擊性能。用於各種特殊軟性和硬性PVC製品。
Vinnolit® VK 710 is a thermoplastic elastomer (TPE) based on polyvinyl chloride (PVC) and polyacrylate (ACR, roughly 50%) possessing properties of PVC and rubber. It is used for all kinds of flexible PVC and hard PVC with impact resistance applications.
|
|
K-240
|
-
|
-
|
高聚合度樹脂、啞光效果。用於特殊薄膜、防黏連助劑。
Vinnolit® K 240 is a high molecular weight specialty product based on micro suspension PVC exhibiting good matting characteristic. It’s used in films and anti-adhesion additives
|